铝 AW-2007 | AlCu4PbMgMn | AW-AlCu4PbMgMn | AlCuMgPb | 3.1645
根据各种标准的铝和铝合金的标记：
| Alu/ | AW-2007 |
| AA | 2007 |
| PN | - |
| CSN | - |
| ASTM USA | - |
| BS GB | - |
| BS GP old | - |
| EN | AlCu4PbMg |
| DIN GER | AlCuMgPb |
| EN | 2007 |
| ISO | AlCu4PbMg |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | - |
| NF FRANCE old | A-U4Pb |
| SFS FINLAND | - |
| SN SWITZ | AlCu4MgPb |
| SS SWEDEN | 4335 |
| UNI ITALY | 9002/8 |
| UNI ITALY old | - |
| UNS | - |
| WNR GERMANY | 3.1645 |
| NS | - |
| UNE | L-3121 |
| ASV | - |
| ALUSUISSE | 2118 |
| CSA old | - |
| GOST old | - |
铝和铝合金的化学成分（根据 EN 573-1）：
| Alu/ | AW-2007 |
| Mg | 0,40 - 1,80 [%] |
| Mn | 0,50 - 1,00 [%] |
| Fe | ≤0,80 [%] |
| Si | ≤0,80 [%] |
| Si+Fe | - [%] |
| Cu | 3,30 - 4,60 [%] |
| Zn | ≤0,80 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,20 [%] |
| Bi | ≤0,20 [%] |
| Ni | ≤0,20 [%] |
| Pb | 0,80 - 1,50 [%] |
| Sn | ≤0,20 [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| 其他 | ≤0,10 [%] |
| 不同在一起 | ≤0,30 [%] |
| Al | reszta |
铝的物理性质：
| - | AW-2007 |
| 密度 | 2.85 [g/cm3] |
| E 弹性模量 | 72500 [MPa] |
| 剪切模量 G | 27300 [MPa] |
| 泊松数 | 0.33 |
| 凝固温度 | 510 [°C] |
| 倾点 | 640 [°C] |
| 恰到好处的温暖 | 856 [J/kgK] |
| 20°C 时的热膨胀系数 | 23 [µm/mK] |
| 电阻率 | 51 [nWm] |
| 导热系数 | 130 [W/mK] |
| 电导率 | 34 [%IACS] |