ALUMINIO AW-5049 | AlMg2Mn0,8 | AW-AlMg2Mn0,8 | AlMg2Mn0,8 | 3.3527
Marcajes de aluminio y aleaciones de aluminio según diversas normas:
| Alu/ | AW-5049 |
| AA | 5049 |
| PN | - |
| CSN | - |
| ASTM USA | - |
| BS GB | - |
| BS GP old | - |
| EN | AlMg2Mn0,8 |
| DIN GER | AlMg2Mn0,8 |
| EN | - |
| ISO | AlMg2Mn0,8 |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | - |
| NF FRANCE old | - |
| SFS FINLAND | - |
| SN SWITZ | - |
| SS SWEDEN | - |
| UNI ITALY | - |
| UNI ITALY old | - |
| UNS | - |
| WNR GERMANY | - |
| NS | - |
| UNE | - |
| ASV | - |
| ALUSUISSE | - |
| CSA old | - |
| GOST old | - |
Composición química del aluminio y aleaciones de aluminio (según EN 573-1):
| Alu/ | AW-5049 |
| Mg | 1,60 - 2,50 [%] |
| Mn | 0,50 - 1,10 [%] |
| Fe | ≤0,50 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,20 [%] |
| Cr | ≤0,30 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,10 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Otro | ≤0,05 [%] |
| diferentes juntos | ≤0,15 [%] |
| Al | reszta |
Propiedades físicas del aluminio:
| - | AW-5049 |
| Densidad | 2.7 [g/cm3] |
| E módulo de elasticidad | 70000 [MPa] |
| Módulo cortante G | 26400 [MPa] |
| número de Poisson | 0.33 |
| Temperatura de solidificación | 615 [°C] |
| punto de fluidez | 650 [°C] |
| El calor adecuado | 896 [J/kgK] |
| Coeficiente de dilatación térmica a 20°C | 23.5 [µm/mK] |
| Resistencia específica | 49.5 [nWm] |
| Conductividad térmica | 138 [W/mK] |
| Conductividad | 35 [%IACS] |