ALUMÍNIUM AW-3103 | AlMn1 | AW-AlMn1 | AlMn1 | 2.0515
Alumínium és alumíniumötvözetek jelölései különböző szabványok szerint:
| Alu/ | AW-3103 |
| AA | 3103 |
| PN | PA1 |
| CSN | 424 432 |
| ASTM USA | - |
| BS GB | 3103 |
| BS GP old | N3 |
| EN | AlMn1 |
| DIN GER | AlMn1 |
| EN | 3103 |
| ISO | AlMn1 |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | - |
| NF FRANCE old | - |
| SFS FINLAND | 2585 |
| SN SWITZ | AlMn |
| SS SWEDEN | 4054 |
| UNI ITALY | 9003/3 |
| UNI ITALY old | 3568 |
| UNS | - |
| WNR GERMANY | 3.0515 |
| NS | 17405 |
| UNE | L-3811 |
| ASV | 2029 |
| ALUSUISSE | 3100 |
| CSA old | M1 |
| GOST old | AMc |
Alumínium és alumíniumötvözetek kémiai összetétele (az EN 573-1 szerint):
| Alu/ | AW-3103 |
| Mg | ≤0,30 [%] |
| Mn | 0,90 - 1,50 [%] |
| Fe | ≤0,70 [%] |
| Si | ≤0,50 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,20 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | ≤0,10 [%] |
| Egyéb | ≤0,05 [%] |
| együtt különböző | ≤0,15 [%] |
| Al | reszta |
Az alumínium fizikai tulajdonságai:
| - | AW-3103 |
| Sűrűség | 2.73 [g/cm3] |
| E rugalmassági modulus | 69500 [MPa] |
| G nyírási modulus | 26100 [MPa] |
| Poisson száma | 0.33 |
| Megszilárdulási hőmérséklet | 640 [°C] |
| Dermedéspontú | 655 [°C] |
| A megfelelő melegség | 892 [J/kgK] |
| Hőtágulási együttható 20°C-on | 23.1 [µm/mK] |
| Fajlagos ellenállás | 41 [nWm] |
| Hővezető | 160 [W/mK] |
| Vezetőképesség | 42 [%IACS] |