ALLUMINIO AW-1200 | Al99,0 | AW-Al99,0 | Al99 | 3.0205
Marcature di alluminio e leghe di alluminio secondo vari standard:
| Alu/ | AW-1200 |
| AA | 1200 |
| PN | A2 |
| CSN | - |
| ASTM USA | - |
| BS GB | 1200 |
| BS GP old | 1C |
| EN | Al99,0 |
| DIN GER | Al99 |
| EN | 1200 |
| ISO | Al99,0 |
| JIS JAPAN | A1200 |
| JIS JAPAN old | A1x3 |
| NF FRANCE | 1200 |
| NF FRANCE old | A4 |
| SFS FINLAND | 2584 |
| SN SWITZ | Al99 |
| SS SWEDEN | 4010 |
| UNI ITALY | 9001/1 |
| UNI ITALY old | 3567 |
| UNS | - |
| WNR GERMANY | 3.0205 |
| NS | 17005 |
| UNE | L-3001 |
| ASV | 1008 |
| ALUSUISSE | 1100 |
| CSA old | 990 |
| GOST old | A/A0 |
Composizione chimica dell alluminio e delle leghe di alluminio (secondo EN 573-1):
| Alu/ | AW-1200 |
| Mg | - [%] |
| Mn | ≤0,05 [%] |
| Fe | - [%] |
| Si | - [%] |
| Si+Fe | ≤1,00 [%] |
| Cu | ≤0,05 [%] |
| Zn | ≤0,10 [%] |
| Cr | - [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,05 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Altro | ≤0,05 [%] |
| diversi insieme | ≤0,15 [%] |
| Al | ≥99,00 |
Proprietà fisiche dell alluminio:
| - | AW-1200 |
| Densità | 2.72 [g/cm3] |
| E modulo di elasticità | 69000 [MPa] |
| Modulo di taglio G | 25900 [MPa] |
| numero di Poisson | 0.33 |
| Temperatura di solidificazione | 645 [°C] |
| Punto di scorrimento | 657 [°C] |
| Il giusto calore | 898 [J/kgK] |
| Coefficiente di dilatazione termica a 20°C | 23.4 [µm/mK] |
| Resistenza specifica | 29.5 [nWm] |
| Conduttività termica | 225 [W/mK] |
| Conducibilità | 58.5 [%IACS] |