アルミニウム AW-2014 | AlCu4SiMg | AW-AlCu4SiMg | AlCuSiMn | 3.1255
さまざまな規格に準拠したアルミニウムおよびアルミニウム合金のマーキング:
| Alu/ | AW-2014 |
| AA | 2014 |
| PN | PA33 |
| CSN | 424 207 |
| ASTM USA | 2014 |
| BS GB | 2014A |
| BS GP old | H15 |
| EN | AlCu4SiMg |
| DIN GER | AlCuSiMn |
| EN | 2014 |
| ISO | AlCu4SiMg |
| JIS JAPAN | A2014 |
| JIS JAPAN old | A3x1 |
| NF FRANCE | 2014 |
| NF FRANCE old | A-U4SG |
| SFS FINLAND | 2595 |
| SN SWITZ | AlCu4SiMn |
| SS SWEDEN | 4338 |
| UNI ITALY | 9002/3 |
| UNI ITALY old | 3581 |
| UNS | A92014 |
| WNR GERMANY | 3.1255 |
| NS | 17105 |
| UNE | L-3130 |
| ASV | - |
| ALUSUISSE | 2662 |
| CSA old | CS41N |
| GOST old | AK8 |
アルミニウムおよびアルミニウム合金の化学組成 (EN 573-1 による):
| Alu/ | AW-2014 |
| Mg | 0,20 - 0,80 [%] |
| Mn | 0,40 - 1,20 [%] |
| Fe | ≤0,70 [%] |
| Si | 0,50 - 1,20 [%] |
| Si+Fe | - [%] |
| Cu | 3,90 - 5,00 [%] |
| Zn | ≤0,25 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,15 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | ≤0,20 [%] |
| 他の | ≤0,05 [%] |
| 一緒に違う | ≤0,15 [%] |
| Al | reszta |
アルミニウムの物理的性質:
| - | AW-2014 O |
| 密度 | 2.8 [g/cm3] |
| E 弾性係数 | 73000 [MPa] |
| せん断弾性率 G | 27400 [MPa] |
| ポアソン数 | 0.33 |
| 凝固温度 | 505 [°C] |
| 流動点 | 640 [°C] |
| 正しい暖かさ | 869 [J/kgK] |
| 20℃での熱膨張係数 | 22.7 [µm/mK] |
| 比抵抗 | 34 [nWm] |
| 熱伝導率 | 192 [W/mK] |
| 導電率 | 50.5 [%IACS] |