ALUMĪNIJA AW-2011 | AlCu6BiPb | AW-AlCu6BiPb | AlCuBiPb | 3.1655
Alumīnija un alumīnija sakausējumu marķējumi atbilstoši dažādiem standartiem:
| Alu/ | AW-2011 |
| AA | 2011 |
| PN | - |
| CSN | - |
| ASTM USA | 2011 |
| BS GB | 2011 |
| BS GP old | FC1 |
| EN | AlCu6BiPb |
| DIN GER | AlCuBiPb |
| EN | 2011 |
| ISO | AlCu6BiPb |
| JIS JAPAN | A2011 |
| JIS JAPAN old | - |
| NF FRANCE | 2011 |
| NF FRANCE old | A-U5PbBi |
| SFS FINLAND | - |
| SN SWITZ | AlCu6BiPb |
| SS SWEDEN | 4355 |
| UNI ITALY | 9002/5 |
| UNI ITALY old | 6362 |
| UNS | A92011 |
| WNR GERMANY | 3.1655 |
| NS | - |
| UNE | L-3192 |
| ASV | - |
| ALUSUISSE | 2500 |
| CSA old | CB60 |
| GOST old | - |
Alumīnija un alumīnija sakausējumu ķīmiskais sastāvs (saskaņā ar EN 573-1):
| Alu/ | AW-2011 |
| Mg | - [%] |
| Mn | - [%] |
| Fe | ≤0,70 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | 5,00 - 6,00 [%] |
| Zn | ≤0,30 [%] |
| Cr | - [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | 0,20 - 0,60 [%] |
| Ni | - [%] |
| Pb | 0,20 - 0,60 [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Cits | ≤0,05 [%] |
| dažādi kopā | ≤0,15 [%] |
| Al | reszta |
Alumīnija fizikālās īpašības:
| - | AW-2011 T3 |
| Blīvums | 2.84 [g/cm3] |
| E elastības modulis | 72500 [MPa] |
| Bīdes modulis G | 27300 [MPa] |
| Puasona numurs | 0.33 |
| Sacietēšanas temperatūra | 540 [°C] |
| Ieliešanas punkts | 645 [°C] |
| Pareizais siltums | 863 [J/kgK] |
| Termiskās izplešanās koeficients pie 20°C | 23 [µm/mK] |
| Specifiskā pretestība | 44 [nWm] |
| Siltumvadītspēja | 152 [W/mK] |
| Vadītspēja | 39 [%IACS] |