ALUMĪNIJA AW-5052 | AlMg2,5 | AW-AlMg2,5 | AlMg2,5 | 3.3523
Alumīnija un alumīnija sakausējumu marķējumi atbilstoši dažādiem standartiem:
| Alu/ | AW-5052 |
| AA | 5052 |
| PN | - |
| CSN | - |
| ASTM USA | 5052 |
| BS GB | - |
| BS GP old | - |
| EN | AlMg2,5 |
| DIN GER | AlMg2,5 |
| EN | 5052 |
| ISO | AlMg2,5 |
| JIS JAPAN | A5052 |
| JIS JAPAN old | A2x1 |
| NF FRANCE | 5052 |
| NF FRANCE old | A-G2.5C |
| SFS FINLAND | 2587 |
| SN SWITZ | AlMg2,5 |
| SS SWEDEN | 4120 |
| UNI ITALY | 9005/2 |
| UNI ITALY old | 3574 |
| UNS | - |
| WNR GERMANY | 3.3523 |
| NS | 17210 |
| UNE | L-3360 |
| ASV | 2041 |
| ALUSUISSE | 5253 |
| CSA old | GR20 |
| GOST old | - |
Alumīnija un alumīnija sakausējumu ķīmiskais sastāvs (saskaņā ar EN 573-1):
| Alu/ | AW-5052 |
| Mg | 2,20 - 2,80 [%] |
| Mn | ≤0,10 [%] |
| Fe | ≤0,40 [%] |
| Si | ≤0,25 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,10 [%] |
| Cr | 0,15 - 0,35 [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Cits | ≤0,05 [%] |
| dažādi kopā | ≤0,15 [%] |
| Al | reszta |
Alumīnija fizikālās īpašības:
| - | AW-5052 |
| Blīvums | 2.7 [g/cm3] |
| E elastības modulis | 69000 [MPa] |
| Bīdes modulis G | 25900 [MPa] |
| Puasona numurs | 0.33 |
| Sacietēšanas temperatūra | 645 [°C] |
| Ieliešanas punkts | 658 [°C] |
| Pareizais siltums | 899 [J/kgK] |
| Termiskās izplešanās koeficients pie 20°C | 23.5 [µm/mK] |
| Specifiskā pretestība | 29 [nWm] |
| Siltumvadītspēja | 229 [W/mK] |
| Vadītspēja | 59.5 [%IACS] |