ALUMINIUM AW-3004 | AlMn1Mg1 | AW-AlMn1Mg1 | AlMn1Mg1 | 3.0526
Merking av aluminium og aluminiumslegeringer i henhold til ulike standarder:
| Alu/ | AW-3004 |
| AA | 3004 |
| PN | PA5 |
| CSN | 424 433 |
| ASTM USA | - |
| BS GB | - |
| BS GP old | - |
| EN | AlMn1Mg1 |
| DIN GER | AlMn1Mg1 |
| EN | - |
| ISO | AlMn1Mg1 |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | - |
| NF FRANCE old | A-MG1 |
| SFS FINLAND | - |
| SN SWITZ | - |
| SS SWEDEN | - |
| UNI ITALY | - |
| UNI ITALY old | 6361 |
| UNS | - |
| WNR GERMANY | - |
| NS | - |
| UNE | L-3820 |
| ASV | - |
| ALUSUISSE | - |
| CSA old | - |
| GOST old | - |
Kjemisk sammensetning av aluminium og aluminiumslegeringer (i henhold til EN 573-1):
| Alu/ | AW-3004 |
| Mg | 0,80 - 1,30 [%] |
| Mn | 1,00 - 1,50 [%] |
| Fe | ≤0,70 [%] |
| Si | ≤0,30 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,25 [%] |
| Zn | ≤0,25 [%] |
| Cr | - [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Annen | ≤0,05 [%] |
| forskjellige sammen | ≤0,15 [%] |
| Al | reszta |
Fysiske egenskaper av aluminium:
| - | AW-3004 |
| Tetthet | 2.72 [g/cm3] |
| E elastisitetsmodul | 70000 [MPa] |
| Skjærmodul G | 26300 [MPa] |
| Poissons nummer | 0.33 |
| Størkningstemperatur | 630 [°C] |
| Hellepunkt | 655 [°C] |
| Den rette varmen | 893 [J/kgK] |
| Termisk utvidelseskoeffisient ved 20°C | 23.3 [µm/mK] |
| Spesifikk motstand | 41 [nWm] |
| Termisk ledningsevne | 160 [W/mK] |
| Konduktivitet | 42 [%IACS] |