АЛЮМИНИЙ AW-6082 | AlMgSiMn | AW-AlSi1MgMn | AlMgSi1 | 3.2315
Маркировка алюминия и алюминиевых сплавов по различным стандартам:
| Alu/ | AW-6082 |
| AA | 6082 |
| PN | PA4 |
| CSN | 424 400 |
| ASTM USA | - |
| BS GB | 6082 |
| BS GP old | H30 |
| EN | AlSi1MgMn |
| DIN GER | AlMgSi1 |
| EN | 6082 |
| ISO | AlSi1MgMn |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | 6082 |
| NF FRANCE old | A-GSM0.7 |
| SFS FINLAND | 2593 |
| SN SWITZ | AlMgSi1Mn |
| SS SWEDEN | 4212 |
| UNI ITALY | 9006/4 |
| UNI ITALY old | 3571 |
| UNS | - |
| WNR GERMANY | 3.2315 |
| NS | 17305 |
| UNE | L-3451 |
| ASV | 2005 |
| ALUSUISSE | 6112 |
| CSA old | SG11R |
| GOST old | AD35 |
Химический состав алюминия и алюминиевых сплавов (согласно EN 573-1):
| Alu/ | AW-6082 |
| Mg | 0,60 - 1,20 [%] |
| Mn | 0,40 - 1,00 [%] |
| Fe | ≤0,50 [%] |
| Si | 0,70 - 1,30 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,20 [%] |
| Cr | ≤0,25 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,10 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Другой | ≤0,05 [%] |
| разные вместе | ≤0,15 [%] |
| Al | reszta |
Физические свойства алюминия:
| - | AW-6082 O |
| Плотность | 2.71 [g/cm3] |
| E модуль упругости | 70000 [MPa] |
| Модуль сдвига G | 26400 [MPa] |
| число Пуассона | 0.33 |
| Температура затвердевания | 575 [°C] |
| Температура застывания | 650 [°C] |
| Правильное тепло | 894 [J/kgK] |
| Коэффициент теплового расширения при 20°C | 23.1 [µm/mK] |
| Удельное сопротивление | 31 [nWm] |
| Теплопроводность | 216 [W/mK] |
| проводимость | 55.5 [%IACS] |