HLINÍK AW-6005A | AlSiMg(A) | AW-AlSiMg(A) | AlMgSi0,7 | 3.3210
Označenie hliníka a hliníkových zliatin podľa rôznych noriem:
| Alu/ | AW-6005A |
| AA | 6005 |
| PN | - |
| CSN | - |
| ASTM USA | - |
| BS GB | - |
| BS GP old | - |
| EN | AlSiMgA |
| DIN GER | AlMgSi0,7 |
| EN | 6005A |
| ISO | AlSiMgA |
| JIS JAPAN | A6NO1 |
| JIS JAPAN old | - |
| NF FRANCE | 6005A |
| NF FRANCE old | A-GS0.5 |
| SFS FINLAND | - |
| SN SWITZ | AlMgSi0,7 |
| SS SWEDEN | - |
| UNI ITALY | 9006/6 |
| UNI ITALY old | - |
| UNS | - |
| WNR GERMANY | 3.3210 |
| NS | - |
| UNE | L-3454 |
| ASV | - |
| ALUSUISSE | 6062 |
| CSA old | - |
| GOST old | - |
Chemické zloženie hliníka a hliníkových zliatin (podľa EN 573-1):
| Alu/ | AW-6005A |
| Mg | 0,40 - 0,70 [%] |
| Mn | ≤0,50 [%] |
| Fe | ≤0,35 [%] |
| Si | 0,50 - 0,90 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,30 [%] |
| Zn | ≤0,20 [%] |
| Cr | ≤0,30 [%] |
| Mn+Cr | 0,12 - 0,50 [%] |
| Ti | ≤0,10 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Iné | ≤0,05 [%] |
| rôzne spolu | ≤0,15 [%] |
| Al | reszta |
Fyzikálne vlastnosti hliníka:
| - | AW-6005A |
| Hustota | 2.71 [g/cm3] |
| E modul pružnosti | 69500 [MPa] |
| Modul šmyku G | 26200 [MPa] |
| Poissonovo číslo | 0.33 |
| Teplota tuhnutia | 605 [°C] |
| Bod liatia | 655 [°C] |
| To správne teplo | 892 [J/kgK] |
| Koeficient tepelnej rozťažnosti pri 20°C | 23.3 [µm/mK] |
| Špecifický odpor | 35 [nWm] |
| Tepelná vodivosť | 193 [W/mK] |
| Vodivosť | 49.5 [%IACS] |