ALUMINIUM AW-1050A | Al99,5 | AW-Al99,5 | Al99,5 | 3.0255
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-1050A |
| AA | 1050 |
| PN | A1 |
| CSN | 424 005 |
| ASTM USA | 1050 |
| BS GB | 1050A |
| BS GP old | 1B |
| EN | Al99,5 |
| DIN GER | Al99,5 |
| EN | 1050A |
| ISO | Al99,5 |
| JIS JAPAN | A1050 |
| JIS JAPAN old | A1x1 |
| NF FRANCE | 1050A |
| NF FRANCE old | A5 |
| SFS FINLAND | 2582 |
| SN SWITZ | Al99,5 |
| SS SWEDEN | 4007 |
| UNI ITALY | 9001/2 |
| UNI ITALY old | 4507 |
| UNS | A91050 |
| WNR GERMANY | 3.0255 |
| NS | 17010 |
| UNE | L-3051 |
| ASV | 1005 |
| ALUSUISSE | 1500 |
| CSA old | 9950 |
| GOST old | A5/ADO |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-1050A |
| Mg | ≤0,05 [%] |
| Mn | ≤0,05 [%] |
| Fe | ≤0,40 [%] |
| Si | ≤0,25 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,05 [%] |
| Zn | ≤0,07 [%] |
| Cr | - [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,05 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,03 [%] |
| différent ensemble | - [%] |
| Al | ≥99,50 |
Propriétés physiques de laluminium :
| - | AW-1050A H24 |
| Densité | 2.7 [g/cm3] |
| E module délasticité | 69000 [MPa] |
| Module de cisaillement G | 25900 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 645 [°C] |
| Point découlement | 658 [°C] |
| La bonne chaleur | 899 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.5 [µm/mK] |
| Résistance spécifique | 29 [nWm] |
| Conductivité thermique | 229 [W/mK] |
| Conductivité | 59.5 [%IACS] |