ALUMINIUM AW-1200 | Al99,0 | AW-Al99,0 | Al99 | 3.0205
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-1200 |
| AA | 1200 |
| PN | A2 |
| CSN | - |
| ASTM USA | - |
| BS GB | 1200 |
| BS GP old | 1C |
| EN | Al99,0 |
| DIN GER | Al99 |
| EN | 1200 |
| ISO | Al99,0 |
| JIS JAPAN | A1200 |
| JIS JAPAN old | A1x3 |
| NF FRANCE | 1200 |
| NF FRANCE old | A4 |
| SFS FINLAND | 2584 |
| SN SWITZ | Al99 |
| SS SWEDEN | 4010 |
| UNI ITALY | 9001/1 |
| UNI ITALY old | 3567 |
| UNS | - |
| WNR GERMANY | 3.0205 |
| NS | 17005 |
| UNE | L-3001 |
| ASV | 1008 |
| ALUSUISSE | 1100 |
| CSA old | 990 |
| GOST old | A/A0 |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-1200 |
| Mg | - [%] |
| Mn | ≤0,05 [%] |
| Fe | - [%] |
| Si | - [%] |
| Si+Fe | ≤1,00 [%] |
| Cu | ≤0,05 [%] |
| Zn | ≤0,10 [%] |
| Cr | - [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,05 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | ≥99,00 |
Propriétés physiques de laluminium :
| - | AW-1200 |
| Densité | 2.72 [g/cm3] |
| E module délasticité | 69000 [MPa] |
| Module de cisaillement G | 25900 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 645 [°C] |
| Point découlement | 657 [°C] |
| La bonne chaleur | 898 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.4 [µm/mK] |
| Résistance spécifique | 29.5 [nWm] |
| Conductivité thermique | 225 [W/mK] |
| Conductivité | 58.5 [%IACS] |