ALUMINIUM AW-2011 | AlCu6BiPb | AW-AlCu6BiPb | AlCuBiPb | 3.1655
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-2011 |
| AA | 2011 |
| PN | - |
| CSN | - |
| ASTM USA | 2011 |
| BS GB | 2011 |
| BS GP old | FC1 |
| EN | AlCu6BiPb |
| DIN GER | AlCuBiPb |
| EN | 2011 |
| ISO | AlCu6BiPb |
| JIS JAPAN | A2011 |
| JIS JAPAN old | - |
| NF FRANCE | 2011 |
| NF FRANCE old | A-U5PbBi |
| SFS FINLAND | - |
| SN SWITZ | AlCu6BiPb |
| SS SWEDEN | 4355 |
| UNI ITALY | 9002/5 |
| UNI ITALY old | 6362 |
| UNS | A92011 |
| WNR GERMANY | 3.1655 |
| NS | - |
| UNE | L-3192 |
| ASV | - |
| ALUSUISSE | 2500 |
| CSA old | CB60 |
| GOST old | - |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-2011 |
| Mg | - [%] |
| Mn | - [%] |
| Fe | ≤0,70 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | 5,00 - 6,00 [%] |
| Zn | ≤0,30 [%] |
| Cr | - [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | 0,20 - 0,60 [%] |
| Ni | - [%] |
| Pb | 0,20 - 0,60 [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-2011 T3 |
| Densité | 2.84 [g/cm3] |
| E module délasticité | 72500 [MPa] |
| Module de cisaillement G | 27300 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 540 [°C] |
| Point découlement | 645 [°C] |
| La bonne chaleur | 863 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23 [µm/mK] |
| Résistance spécifique | 44 [nWm] |
| Conductivité thermique | 152 [W/mK] |
| Conductivité | 39 [%IACS] |