ALUMINIUM AW-2014 | AlCu4SiMg | AW-AlCu4SiMg | AlCuSiMn | 3.1255
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-2014 |
| AA | 2014 |
| PN | PA33 |
| CSN | 424 207 |
| ASTM USA | 2014 |
| BS GB | 2014A |
| BS GP old | H15 |
| EN | AlCu4SiMg |
| DIN GER | AlCuSiMn |
| EN | 2014 |
| ISO | AlCu4SiMg |
| JIS JAPAN | A2014 |
| JIS JAPAN old | A3x1 |
| NF FRANCE | 2014 |
| NF FRANCE old | A-U4SG |
| SFS FINLAND | 2595 |
| SN SWITZ | AlCu4SiMn |
| SS SWEDEN | 4338 |
| UNI ITALY | 9002/3 |
| UNI ITALY old | 3581 |
| UNS | A92014 |
| WNR GERMANY | 3.1255 |
| NS | 17105 |
| UNE | L-3130 |
| ASV | - |
| ALUSUISSE | 2662 |
| CSA old | CS41N |
| GOST old | AK8 |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-2014 |
| Mg | 0,20 - 0,80 [%] |
| Mn | 0,40 - 1,20 [%] |
| Fe | ≤0,70 [%] |
| Si | 0,50 - 1,20 [%] |
| Si+Fe | - [%] |
| Cu | 3,90 - 5,00 [%] |
| Zn | ≤0,25 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,15 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | ≤0,20 [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-2014 O |
| Densité | 2.8 [g/cm3] |
| E module délasticité | 73000 [MPa] |
| Module de cisaillement G | 27400 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 505 [°C] |
| Point découlement | 640 [°C] |
| La bonne chaleur | 869 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 22.7 [µm/mK] |
| Résistance spécifique | 34 [nWm] |
| Conductivité thermique | 192 [W/mK] |
| Conductivité | 50.5 [%IACS] |