ALUMINIUM AW-2017A | AlCu4MgSi | AW-AlCu4MgSi | AlCuMg1 | 3.1325
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-2017A |
| AA | 2017 |
| PN | PA6 |
| CSN | 424 201 |
| ASTM USA | 2017 |
| BS GB | 2017A |
| BS GP old | - |
| EN | AlCu4MgSiA |
| DIN GER | AlCuMg1 |
| EN | 2017A |
| ISO | AlCu4MgSiA |
| JIS JAPAN | A2017 |
| JIS JAPAN old | A3x2 |
| NF FRANCE | 2017A |
| NF FRANCE old | A-U4G |
| SFS FINLAND | - |
| SN SWITZ | - |
| SS SWEDEN | - |
| UNI ITALY | 9002/2 |
| UNI ITALY old | 3579 |
| UNS | A92017 |
| WNR GERMANY | 3.1325 |
| NS | - |
| UNE | L-3120 |
| ASV | - |
| ALUSUISSE | 2100 |
| CSA old | CM41 |
| GOST old | D1/V65 |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-2017A |
| Mg | 0,40 - 1,00 [%] |
| Mn | 0,40 - 1,00 [%] |
| Fe | ≤0,70 [%] |
| Si | 0,20 - 0,80 [%] |
| Si+Fe | - [%] |
| Cu | 3,50 - 4,50 [%] |
| Zn | ≤0,25 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | ≤0,25 [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-2017A T4 |
| Densité | 2.8 [g/cm3] |
| E module délasticité | 72500 [MPa] |
| Module de cisaillement G | 27200 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 510 [°C] |
| Point découlement | 645 [°C] |
| La bonne chaleur | 873 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 22.9 [µm/mK] |
| Résistance spécifique | 51 [nWm] |
| Conductivité thermique | 134 [W/mK] |
| Conductivité | 34 [%IACS] |