ALUMINIUM AW-3004 | AlMn1Mg1 | AW-AlMn1Mg1 | AlMn1Mg1 | 3.0526
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-3004 |
| AA | 3004 |
| PN | PA5 |
| CSN | 424 433 |
| ASTM USA | - |
| BS GB | - |
| BS GP old | - |
| EN | AlMn1Mg1 |
| DIN GER | AlMn1Mg1 |
| EN | - |
| ISO | AlMn1Mg1 |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | - |
| NF FRANCE old | A-MG1 |
| SFS FINLAND | - |
| SN SWITZ | - |
| SS SWEDEN | - |
| UNI ITALY | - |
| UNI ITALY old | 6361 |
| UNS | - |
| WNR GERMANY | - |
| NS | - |
| UNE | L-3820 |
| ASV | - |
| ALUSUISSE | - |
| CSA old | - |
| GOST old | - |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-3004 |
| Mg | 0,80 - 1,30 [%] |
| Mn | 1,00 - 1,50 [%] |
| Fe | ≤0,70 [%] |
| Si | ≤0,30 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,25 [%] |
| Zn | ≤0,25 [%] |
| Cr | - [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-3004 |
| Densité | 2.72 [g/cm3] |
| E module délasticité | 70000 [MPa] |
| Module de cisaillement G | 26300 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 630 [°C] |
| Point découlement | 655 [°C] |
| La bonne chaleur | 893 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.3 [µm/mK] |
| Résistance spécifique | 41 [nWm] |
| Conductivité thermique | 160 [W/mK] |
| Conductivité | 42 [%IACS] |