ALUMINIUM AW-3005 | AlMn1Mg0,5 | AW-AlMn1Mg0,5 | AlMn1Mg0,5 | 3.0525
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-3005 |
| AA | 3005 |
| PN | - |
| CSN | - |
| ASTM USA | - |
| BS GB | - |
| BS GP old | - |
| EN | AlMn1Mg0,5 |
| DIN GER | AlMn1Mg0,5 |
| EN | - |
| ISO | AlMn1Mg0,5 |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | - |
| NF FRANCE old | A-MG0,5 |
| SFS FINLAND | - |
| SN SWITZ | - |
| SS SWEDEN | - |
| UNI ITALY | - |
| UNI ITALY old | - |
| UNS | - |
| WNR GERMANY | - |
| NS | - |
| UNE | - |
| ASV | - |
| ALUSUISSE | - |
| CSA old | - |
| GOST old | - |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-3005 |
| Mg | 0,20 - 0,60 [%] |
| Mn | 1,00 - 1,50 [%] |
| Fe | ≤0,70 [%] |
| Si | ≤0,60 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,30 [%] |
| Zn | ≤0,25 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,10 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-3005 |
| Densité | 2.73 [g/cm3] |
| E module délasticité | 69500 [MPa] |
| Module de cisaillement G | 26200 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 635 [°C] |
| Point découlement | 655 [°C] |
| La bonne chaleur | 891 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.1 [µm/mK] |
| Résistance spécifique | 41 [nWm] |
| Conductivité thermique | 160 [W/mK] |
| Conductivité | 42 [%IACS] |