ALUMINIUM AW-3103 | AlMn1 | AW-AlMn1 | AlMn1 | 2.0515
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-3103 |
| AA | 3103 |
| PN | PA1 |
| CSN | 424 432 |
| ASTM USA | - |
| BS GB | 3103 |
| BS GP old | N3 |
| EN | AlMn1 |
| DIN GER | AlMn1 |
| EN | 3103 |
| ISO | AlMn1 |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | - |
| NF FRANCE old | - |
| SFS FINLAND | 2585 |
| SN SWITZ | AlMn |
| SS SWEDEN | 4054 |
| UNI ITALY | 9003/3 |
| UNI ITALY old | 3568 |
| UNS | - |
| WNR GERMANY | 3.0515 |
| NS | 17405 |
| UNE | L-3811 |
| ASV | 2029 |
| ALUSUISSE | 3100 |
| CSA old | M1 |
| GOST old | AMc |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-3103 |
| Mg | ≤0,30 [%] |
| Mn | 0,90 - 1,50 [%] |
| Fe | ≤0,70 [%] |
| Si | ≤0,50 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,20 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | ≤0,10 [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-3103 |
| Densité | 2.73 [g/cm3] |
| E module délasticité | 69500 [MPa] |
| Module de cisaillement G | 26100 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 640 [°C] |
| Point découlement | 655 [°C] |
| La bonne chaleur | 892 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.1 [µm/mK] |
| Résistance spécifique | 41 [nWm] |
| Conductivité thermique | 160 [W/mK] |
| Conductivité | 42 [%IACS] |