ALUMINIUM AW-5052 | AlMg2,5 | AW-AlMg2,5 | AlMg2,5 | 3.3523
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-5052 |
| AA | 5052 |
| PN | - |
| CSN | - |
| ASTM USA | 5052 |
| BS GB | - |
| BS GP old | - |
| EN | AlMg2,5 |
| DIN GER | AlMg2,5 |
| EN | 5052 |
| ISO | AlMg2,5 |
| JIS JAPAN | A5052 |
| JIS JAPAN old | A2x1 |
| NF FRANCE | 5052 |
| NF FRANCE old | A-G2.5C |
| SFS FINLAND | 2587 |
| SN SWITZ | AlMg2,5 |
| SS SWEDEN | 4120 |
| UNI ITALY | 9005/2 |
| UNI ITALY old | 3574 |
| UNS | - |
| WNR GERMANY | 3.3523 |
| NS | 17210 |
| UNE | L-3360 |
| ASV | 2041 |
| ALUSUISSE | 5253 |
| CSA old | GR20 |
| GOST old | - |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-5052 |
| Mg | 2,20 - 2,80 [%] |
| Mn | ≤0,10 [%] |
| Fe | ≤0,40 [%] |
| Si | ≤0,25 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,10 [%] |
| Cr | 0,15 - 0,35 [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-5052 |
| Densité | 2.7 [g/cm3] |
| E module délasticité | 69000 [MPa] |
| Module de cisaillement G | 25900 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 645 [°C] |
| Point découlement | 658 [°C] |
| La bonne chaleur | 899 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.5 [µm/mK] |
| Résistance spécifique | 29 [nWm] |
| Conductivité thermique | 229 [W/mK] |
| Conductivité | 59.5 [%IACS] |