ALUMINIUM AW-5083 | AlMg4,5Mn0,7 | AW-AlMg4,5Mn0,7 | AlMg4,5Mn | 3.3547
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-5083 |
| AA | 5083 |
| PN | PA13 |
| CSN | - |
| ASTM USA | 5083 |
| BS GB | 5083 |
| BS GP old | N8 |
| EN | AlMg4,5Mn0,7 |
| DIN GER | AlMg4,5Mn |
| EN | 5083 |
| ISO | AlMg4,5Mn0,7 |
| JIS JAPAN | A5083 |
| JIS JAPAN old | A2x7 |
| NF FRANCE | 5083 |
| NF FRANCE old | A-G4.5MC |
| SFS FINLAND | - |
| SN SWITZ | AlMg4,5Mn |
| SS SWEDEN | 4140 |
| UNI ITALY | 9005/5 |
| UNI ITALY old | 7790 |
| UNS | A95083 |
| WNR GERMANY | 3.3547 |
| NS | 17215 |
| UNE | L-3321 |
| ASV | 2021 |
| ALUSUISSE | 5460 |
| CSA old | GM41 |
| GOST old | - |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-5083 |
| Mg | 4,00 - 4,90 [%] |
| Mn | 0,40 - 1,00 [%] |
| Fe | ≤0,40 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,25 [%] |
| Cr | 0,05 - 0,25 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,15 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-5083 |
| Densité | 2.7 [g/cm3] |
| E module délasticité | 71000 [MPa] |
| Module de cisaillement G | 26800 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 580 [°C] |
| Point découlement | 640 [°C] |
| La bonne chaleur | 899 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.8 [µm/mK] |
| Résistance spécifique | 60 [nWm] |
| Conductivité thermique | 117 [W/mK] |
| Conductivité | 28.5 [%IACS] |