ALUMINIUM AW-5251 | AlMg2 | AW-AlMg2 | AlMg2Mn0,3 | 3.3525
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-5251 |
| AA | 5251 |
| PN | PA2 |
| CSN | 424 412 |
| ASTM USA | - |
| BS GB | 5251 |
| BS GP old | N4 |
| EN | AlMg2 |
| DIN GER | AlMg2Mn0,3 |
| EN | 5251 |
| ISO | AlMg2 |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | 5251 |
| NF FRANCE old | A-G2M |
| SFS FINLAND | - |
| SN SWITZ | - |
| SS SWEDEN | - |
| UNI ITALY | - |
| UNI ITALY old | - |
| UNS | - |
| WNR GERMANY | 3.3525 |
| NS | 17205 |
| UNE | L-3361 |
| ASV | 2023 |
| ALUSUISSE | 5200 |
| CSA old | - |
| GOST old | AMg2 |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-5251 |
| Mg | 1,70 - 2,40 [%] |
| Mn | 0,10 - 0,50 [%] |
| Fe | ≤0,50 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,15 [%] |
| Zn | ≤0,15 [%] |
| Cr | ≤0,15 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,15 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-5251 |
| Densité | 2.7 [g/cm3] |
| E module délasticité | 70000 [MPa] |
| Module de cisaillement G | 26300 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 605 [°C] |
| Point découlement | 650 [°C] |
| La bonne chaleur | 898 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.6 [µm/mK] |
| Résistance spécifique | 46 [nWm] |
| Conductivité thermique | 149 [W/mK] |
| Conductivité | 37.5 [%IACS] |