ALUMINIUM AW-5754 | AlMg3 | AW-AlMg3 | AlMg3 | 3.3535
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-5754 |
| AA | 5754 |
| PN | PA11 |
| CSN | 424 413 |
| ASTM USA | - |
| BS GB | - |
| BS GP old | - |
| EN | AlMg3 |
| DIN GER | AlMg3 |
| EN | 5754 |
| ISO | AlMg3 |
| JIS JAPAN | - |
| JIS JAPAN old | - |
| NF FRANCE | 5754 |
| NF FRANCE old | A-G3M |
| SFS FINLAND | 2588 |
| SN SWITZ | AlMg3 |
| SS SWEDEN | 4125 |
| UNI ITALY | - |
| UNI ITALY old | - |
| UNS | - |
| WNR GERMANY | 3.3535 |
| NS | - |
| UNE | L-3390 |
| ASV | 2014 |
| ALUSUISSE | 5300 |
| CSA old | - |
| GOST old | AMg3 |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-5754 |
| Mg | 2,60 - 3,60 [%] |
| Mn | ≤0,50 [%] |
| Fe | ≤0,40 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,20 [%] |
| Cr | ≤0,30 [%] |
| Mn+Cr | 0,10 - 0,60 [%] |
| Ti | ≤0,15 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-5754 H111 |
| Densité | 2.7 [g/cm3] |
| E module délasticité | 70500 [MPa] |
| Module de cisaillement G | 26500 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 595 [°C] |
| Point découlement | 645 [°C] |
| La bonne chaleur | 897 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.7 [µm/mK] |
| Résistance spécifique | 53 [nWm] |
| Conductivité thermique | 132 [W/mK] |
| Conductivité | 32.5 [%IACS] |