ALUMINIUM AW-6061 | AlMg1SiCu | AW-AlMg1SiCu | AlMg1SiCu | 3.3211
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-6061 |
| AA | 6061 |
| PN | PA45 |
| CSN | - |
| ASTM USA | 6061 |
| BS GB | 6061 |
| BS GP old | H20 |
| EN | AlMg1SiCu |
| DIN GER | AlMg1SiCu |
| EN | 6061 |
| ISO | AlMg1SiCu |
| JIS JAPAN | A6061 |
| JIS JAPAN old | A2x4 |
| NF FRANCE | 6061 |
| NF FRANCE old | A-GSUC |
| SFS FINLAND | - |
| SN SWITZ | - |
| SS SWEDEN | - |
| UNI ITALY | 9006/2 |
| UNI ITALY old | 6170 |
| UNS | A96061 |
| WNR GERMANY | 3.3211 |
| NS | - |
| UNE | L-3420 |
| ASV | 2079 |
| ALUSUISSE | 6061 |
| CSA old | GS11N |
| GOST old | AD33/AV |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-6061 |
| Mg | 0,80 - 1,20 [%] |
| Mn | ≤0,15 [%] |
| Fe | ≤0,70 [%] |
| Si | 0,40 - 0,80 [%] |
| Si+Fe | - [%] |
| Cu | 0,15 - 0,40 [%] |
| Zn | ≤0,25 [%] |
| Cr | 0,04 - 0,35 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,15 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-6061 O |
| Densité | 2.7 [g/cm3] |
| E module délasticité | 70000 [MPa] |
| Module de cisaillement G | 26300 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 580 [°C] |
| Point découlement | 650 [°C] |
| La bonne chaleur | 895 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.3 [µm/mK] |
| Résistance spécifique | 37 [nWm] |
| Conductivité thermique | 180 [W/mK] |
| Conductivité | 46.5 [%IACS] |