ALUMINIUM AW-6063 | AlMg0,7Si | AW-AlMg0,7Si
Marquages daluminium et dalliages daluminium selon diverses normes :
| Alu/ | AW-6063 |
| AA | 6063 |
| PN | PA38 |
| CSN | 424 401 |
| ASTM USA | 6063 |
| BS GB | 6063 |
| BS GP old | H9 |
| EN | AlMg0,7Si |
| DIN GER | AlMgSi0,5 |
| EN | 6063 |
| ISO | AlMg0,7Si |
| JIS JAPAN | A6063 |
| JIS JAPAN old | A2x5 |
| NF FRANCE | - |
| NF FRANCE old | A-GS |
| SFS FINLAND | 2591 |
| SN SWITZ | - |
| SS SWEDEN | 4104 |
| UNI ITALY | - |
| UNI ITALY old | 3569 |
| UNS | - |
| WNR GERMANY | 3.3206 |
| NS | 17310 |
| UNE | L-3441 |
| ASV | 2032 |
| ALUSUISSE | 6050 |
| CSA old | GS10 |
| GOST old | AD31 |
Composition chimique de laluminium et des alliages daluminium (selon EN 573-1) :
| Alu/ | AW-6063 |
| Mg | 0,45 - 0,90 [%] |
| Mn | ≤0,10 [%] |
| Fe | ≤0,35 [%] |
| Si | 0,20 - 0,60 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,10 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,10 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Autre | ≤0,05 [%] |
| différent ensemble | ≤0,15 [%] |
| Al | reszta |
Propriétés physiques de laluminium :
| - | AW-6063 O |
| Densité | 2.7 [g/cm3] |
| E module délasticité | 69500 [MPa] |
| Module de cisaillement G | 26100 [MPa] |
| nombre de Poisson | 0.33 |
| Température de solidification | 615 [°C] |
| Point découlement | 655 [°C] |
| La bonne chaleur | 898 [J/kgK] |
| Coefficient de dilatation thermique à 20°C | 23.5 [µm/mK] |
| Résistance spécifique | 30 [nWm] |
| Conductivité thermique | 218 [W/mK] |
| Conductivité | 57.5 [%IACS] |