blacha aluminiowa AW-1050A H24 0,50 x 1000,00 x 2000,00 mm
Stop | AW-1050A | |
Stan | H24 | |
Wymiary / Wagi: | ||
A | 0,50 [mm] | |
B | 1000,00 [mm] | |
C | 2000,00 [mm] | |
Waga 1 m2 | 1,35 [kg] | |
Waga arkusza | 2,70 [kg] |
Informacje techniczne
Oznaczenia aluminium/stopu wg innych norm:
AA | 1050 |
PN | A1 |
CSN | 424 005 |
ASTM USA | 1050 |
BS GB | 1050A |
BS GP old | 1B |
EN | Al99,5 |
DIN GER | Al99,5 |
EN | 1050A |
ISO | Al99,5 |
JIS JAPAN | A1050 |
JIS JAPAN old | A1x1 |
NF FRANCE | 1050A |
NF FRANCE old | A5 |
SFS FINLAND | 2582 |
SN SWITZ | Al99,5 |
SS SWEDEN | 4007 |
UNI ITALY | 9001/2 |
UNI ITALY old | 4507 |
UNS | A91050 |
WNR GERMANY | 3.0255 |
NS | 17010 |
UNE | L-3051 |
ASV | 1005 |
ALUSUISSE | 1500 |
CSA old | 9950 |
GOST old | A5/ADO |
Skład chemiczny zgodnie z normą EN 573-1:
Mg | ≤0,05 [%] |
Mn | ≤0,05 [%] |
Fe | ≤0,40 [%] |
Si | ≤0,25 [%] |
Si+Fe | - [%] |
Cu | ≤0,05 [%] |
Zn | ≤0,07 [%] |
Cr | - [%] |
Mn+Cr | - [%] |
Ti | ≤0,05 [%] |
Bi | - [%] |
Ni | - [%] |
Pb | - [%] |
Sn | - [%] |
Zr | - [%] |
Zr+Ti | - [%] |
Inne | ≤0,03 [%] |
Inne razem | - [%] |
Al | ≥99,50 |
Właściwości fizyczne aluminium:
Gęstość | 2.7 [g/cm3] |
Moduł sprężystości E | 69000 [MPa] |
Moduł sprężystości poprzecznej G | 25900 [MPa] |
Liczba Poissona | 0.33 |
Temperatura krzepnięcia | 645 [°C] |
Temperatura płynięcia | 658 [°C] |
Ciepło właściwe w 20 °C | 899 [J/kgK] |
Współczynnik rozszerzalności cieplnej w 20°C | 23.5 [µm/mK] |
Opór właściwy | 29 [nWm] |
Przewodność cieplna | 229 [W/mK] |
Przewodność elektryczna | 59.5 [%IACS] |
Własności wytrzymałościowe zgodnie z normą EN 485-2:
Wytrzymałość na rozciąganie Rm min. | 105 [MPa] |
Wytrzymałość na rozciąganie Rm max. | 145 [MPa] |
Granica plastyczności Rp02 min. | 75 [MPa] |
Granica plastyczności Rp02 max. | - [MPa] |
Wydłużenie min. A50mm | 4 [%] |
Wydłużenie min. A | - [%] |
Promień gięcia 180° | 1.0t |
Promień gięcia 90° | 0.5t |
Twardość w skali Brinella | 33 [HB] |