Blacha aluminiowa AW-2017A T4/T451 5,00 x 1000,00 x 2000,00 mm
| Stop | AW-2017A | |
| Stan | T4/T451 | |
| Wymiary / Wagi: | ||
| A | 5,00 [mm] | |
| B | 1000,00 [mm] | |
| C | 2000,00 [mm] | |
| Waga 1 m2 | 14,00 [kg] | |
| Waga arkusza | 28,00 [kg] | |
Informacje techniczne
Oznaczenia aluminium/stopu wg innych norm:
| AA | 2017 |
| PN | PA6 |
| CSN | 424 201 |
| ASTM USA | 2017 |
| BS GB | 2017A |
| BS GP old | - |
| EN | AlCu4MgSiA |
| DIN GER | AlCuMg1 |
| EN | 2017A |
| ISO | AlCu4MgSiA |
| JIS JAPAN | A2017 |
| JIS JAPAN old | A3x2 |
| NF FRANCE | 2017A |
| NF FRANCE old | A-U4G |
| SFS FINLAND | - |
| SN SWITZ | - |
| SS SWEDEN | - |
| UNI ITALY | 9002/2 |
| UNI ITALY old | 3579 |
| UNS | A92017 |
| WNR GERMANY | 3.1325 |
| NS | - |
| UNE | L-3120 |
| ASV | - |
| ALUSUISSE | 2100 |
| CSA old | CM41 |
| GOST old | D1/V65 |
Skład chemiczny zgodnie z normą EN 573-1:
| Mg | 0,40 - 1,00 [%] |
| Mn | 0,40 - 1,00 [%] |
| Fe | ≤0,70 [%] |
| Si | 0,20 - 0,80 [%] |
| Si+Fe | - [%] |
| Cu | 3,50 - 4,50 [%] |
| Zn | ≤0,25 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | ≤0,25 [%] |
| Inne | ≤0,05 [%] |
| Inne razem | ≤0,15 [%] |
| Al | reszta |
Własności wytrzymałościowe zgodnie z normą EN 485-2:
| Wytrzymałość na rozciąganie Rm min. | 390 [MPa] |
| Wytrzymałość na rozciąganie Rm max. | - [MPa] |
| Granica plastyczności Rp02 min. | 245 [MPa] |
| Granica plastyczności Rp02 max. | - [MPa] |
| Wydłużenie min. A50mm | 15 [%] |
| Wydłużenie min. A | - [%] |
| Promień gięcia 180° | 5.0t |
| Promień gięcia 90° | 5.0t |
| Twardość w skali Brinella | 110 [HB] |