blacha aluminiowa AW-2017A T4/T451 1,50 x 1000,00 x 2000,00 mm
Stop | AW-2017A | |
Stan | T4/T451 | |
Wymiary / Wagi: | ||
A | 1,50 [mm] | |
B | 1000,00 [mm] | |
C | 2000,00 [mm] | |
Waga 1 m2 | 4,20 [kg] | |
Waga arkusza | 8,40 [kg] |
Informacje techniczne
Oznaczenia aluminium/stopu wg innych norm:
AA | 2017 |
PN | PA6 |
CSN | 424 201 |
ASTM USA | 2017 |
BS GB | 2017A |
BS GP old | - |
EN | AlCu4MgSiA |
DIN GER | AlCuMg1 |
EN | 2017A |
ISO | AlCu4MgSiA |
JIS JAPAN | A2017 |
JIS JAPAN old | A3x2 |
NF FRANCE | 2017A |
NF FRANCE old | A-U4G |
SFS FINLAND | - |
SN SWITZ | - |
SS SWEDEN | - |
UNI ITALY | 9002/2 |
UNI ITALY old | 3579 |
UNS | A92017 |
WNR GERMANY | 3.1325 |
NS | - |
UNE | L-3120 |
ASV | - |
ALUSUISSE | 2100 |
CSA old | CM41 |
GOST old | D1/V65 |
Skład chemiczny zgodnie z normą EN 573-1:
Mg | 0,40 - 1,00 [%] |
Mn | 0,40 - 1,00 [%] |
Fe | ≤0,70 [%] |
Si | 0,20 - 0,80 [%] |
Si+Fe | - [%] |
Cu | 3,50 - 4,50 [%] |
Zn | ≤0,25 [%] |
Cr | ≤0,10 [%] |
Mn+Cr | - [%] |
Ti | - [%] |
Bi | - [%] |
Ni | - [%] |
Pb | - [%] |
Sn | - [%] |
Zr | - [%] |
Zr+Ti | ≤0,25 [%] |
Inne | ≤0,05 [%] |
Inne razem | ≤0,15 [%] |
Al | reszta |
Własności wytrzymałościowe zgodnie z normą EN 485-2:
Wytrzymałość na rozciąganie Rm min. | 390 [MPa] |
Wytrzymałość na rozciąganie Rm max. | - [MPa] |
Granica plastyczności Rp02 min. | 245 [MPa] |
Granica plastyczności Rp02 max. | - [MPa] |
Wydłużenie min. A50mm | 15 [%] |
Wydłużenie min. A | - [%] |
Promień gięcia 180° | 5.0t |
Promień gięcia 90° | 5.0t |
Twardość w skali Brinella | 110 [HB] |