blacha aluminiowa AW-5754 H111 8,00 x 1000,00 x 2000,00 mm
Stop | AW-5754 | |
Stan | H111 | |
Wymiary / Wagi: | ||
A | 8,00 [mm] | |
B | 1000,00 [mm] | |
C | 2000,00 [mm] | |
Waga 1 m2 | 21,60 [kg] | |
Waga arkusza | 43,20 [kg] |
Informacje techniczne
Oznaczenia aluminium/stopu wg innych norm:
AA | 5754 |
PN | PA11 |
CSN | 424 413 |
ASTM USA | - |
BS GB | - |
BS GP old | - |
EN | AlMg3 |
DIN GER | AlMg3 |
EN | 5754 |
ISO | AlMg3 |
JIS JAPAN | - |
JIS JAPAN old | - |
NF FRANCE | 5754 |
NF FRANCE old | A-G3M |
SFS FINLAND | 2588 |
SN SWITZ | AlMg3 |
SS SWEDEN | 4125 |
UNI ITALY | - |
UNI ITALY old | - |
UNS | - |
WNR GERMANY | 3.3535 |
NS | - |
UNE | L-3390 |
ASV | 2014 |
ALUSUISSE | 5300 |
CSA old | - |
GOST old | AMg3 |
Skład chemiczny zgodnie z normą EN 573-1:
Mg | 2,60 - 3,60 [%] |
Mn | ≤0,50 [%] |
Fe | ≤0,40 [%] |
Si | ≤0,40 [%] |
Si+Fe | - [%] |
Cu | ≤0,10 [%] |
Zn | ≤0,20 [%] |
Cr | ≤0,30 [%] |
Mn+Cr | 0,10 - 0,60 [%] |
Ti | ≤0,15 [%] |
Bi | - [%] |
Ni | - [%] |
Pb | - [%] |
Sn | - [%] |
Zr | - [%] |
Zr+Ti | - [%] |
Inne | ≤0,05 [%] |
Inne razem | ≤0,15 [%] |
Al | reszta |
Właściwości fizyczne aluminium:
Gęstość | 2.7 [g/cm3] |
Moduł sprężystości E | 70500 [MPa] |
Moduł sprężystości poprzecznej G | 26500 [MPa] |
Liczba Poissona | 0.33 |
Temperatura krzepnięcia | 595 [°C] |
Temperatura płynięcia | 645 [°C] |
Ciepło właściwe w 20 °C | 897 [J/kgK] |
Współczynnik rozszerzalności cieplnej w 20°C | 23.7 [µm/mK] |
Opór właściwy | 53 [nWm] |
Przewodność cieplna | 132 [W/mK] |
Przewodność elektryczna | 32.5 [%IACS] |