blacha aluminiowa AW-7075 T6/T651 5,00 x 1000,00 x 2000,00 mm
Stop | AW-7075 | |
Stan | T6/T651 | |
Wymiary / Wagi: | ||
A | 5,00 [mm] | |
B | 1000,00 [mm] | |
C | 2000,00 [mm] | |
Waga 1 m2 | 14,05 [kg] | |
Waga arkusza | 28,10 [kg] |
Informacje techniczne
Oznaczenia aluminium/stopu wg innych norm:
AA | 7075 |
PN | PA9 |
CSN | 424 222 |
ASTM USA | 7075 |
BS GB | 7075 |
BS GP old | 2L95 |
EN | AlZn5,5MgCu |
DIN GER | AlZnMgCu1,5 |
EN | 7075 |
ISO | AlZn5,5MgCu |
JIS JAPAN | A7075 |
JIS JAPAN old | A34x6 |
NF FRANCE | 7075 |
NF FRANCE old | A-Z5GU |
SFS FINLAND | - |
SN SWITZ | AlZn6MgCu1,5 |
SS SWEDEN | - |
UNI ITALY | 9007/2 |
UNI ITALY old | 3735 |
UNS | A97075 |
WNR GERMANY | 3.4365 |
NS | - |
UNE | L-3710 |
ASV | 2082 |
ALUSUISSE | 7215 |
CSA old | ZG62 |
GOST old | B95V95 |
Skład chemiczny zgodnie z normą EN 573-1:
Mg | 2,10 - 2,90 [%] |
Mn | ≤0,30 [%] |
Fe | ≤0,50 [%] |
Si | ≤0,40 [%] |
Si+Fe | - [%] |
Cu | 1,20 - 2,00 [%] |
Zn | 5,10 - 6,10 [%] |
Cr | 0,18 - 0,28 [%] |
Mn+Cr | - [%] |
Ti | ≤0,20 [%] |
Bi | - [%] |
Ni | - [%] |
Pb | - [%] |
Sn | - [%] |
Zr | - [%] |
Zr+Ti | ≤0,25 [%] |
Inne | ≤0,05 [%] |
Inne razem | ≤0,15 [%] |
Al | reszta |
Własności wytrzymałościowe zgodnie z normą EN 485-2:
Wytrzymałość na rozciąganie Rm min. | 545 [MPa] |
Wytrzymałość na rozciąganie Rm max. | - [MPa] |
Granica plastyczności Rp02 min. | 475 [MPa] |
Granica plastyczności Rp02 max. | - [MPa] |
Wydłużenie min. A50mm | 8 [%] |
Wydłużenie min. A | - [%] |
Promień gięcia 180° | - |
Promień gięcia 90° | 8.0t |
Twardość w skali Brinella | 163 [HB] |