Pręt aluminiowy okrągły AW-7075 T6 fi 230,00 x 3000,00 mm
| Stop | AW-7075 | |
| Stan | T6 | |
| Wymiary / Wagi: | ||
| fi | 230,00 [mm] | |
| L | 3000,00 [mm] | |
| Waga 1 mb | 116,69 [kg] | |
| Waga pręta | 350,07 [kg] | |
Informacje techniczne
Oznaczenia aluminium/stopu wg innych norm:
| AA | 7075 |
| PN | PA9 |
| CSN | 424 222 |
| ASTM USA | 7075 |
| BS GB | 7075 |
| BS GP old | 2L95 |
| EN | AlZn5,5MgCu |
| DIN GER | AlZnMgCu1,5 |
| EN | 7075 |
| ISO | AlZn5,5MgCu |
| JIS JAPAN | A7075 |
| JIS JAPAN old | A34x6 |
| NF FRANCE | 7075 |
| NF FRANCE old | A-Z5GU |
| SFS FINLAND | - |
| SN SWITZ | AlZn6MgCu1,5 |
| SS SWEDEN | - |
| UNI ITALY | 9007/2 |
| UNI ITALY old | 3735 |
| UNS | A97075 |
| WNR GERMANY | 3.4365 |
| NS | - |
| UNE | L-3710 |
| ASV | 2082 |
| ALUSUISSE | 7215 |
| CSA old | ZG62 |
| GOST old | B95V95 |
Skład chemiczny zgodnie z normą EN 573-1:
| Mg | 2,10 - 2,90 [%] |
| Mn | ≤0,30 [%] |
| Fe | ≤0,50 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | 1,20 - 2,00 [%] |
| Zn | 5,10 - 6,10 [%] |
| Cr | 0,18 - 0,28 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,20 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | ≤0,25 [%] |
| Inne | ≤0,05 [%] |
| Inne razem | ≤0,15 [%] |
| Al | reszta |
Właściwości fizyczne aluminium:
| Gęstość | 2.81 [g/cm3] |
| Moduł sprężystości E | 72000 [MPa] |
| Moduł sprężystości poprzecznej G | 27100 [MPa] |
| Liczba Poissona | 0.33 |
| Temperatura krzepnięcia | 475 [°C] |
| Temperatura płynięcia | 635 [°C] |
| Ciepło właściwe w 20 °C | 862 [J/kgK] |
| Współczynnik rozszerzalności cieplnej w 20°C | 23.5 [µm/mK] |
| Opór właściwy | 52 [nWm] |
| Przewodność cieplna | 134 [W/mK] |
| Przewodność elektryczna | 33 [%IACS] |