ALUMINIUM AW-5005 | AlMg1(B) | AW-AlMg1(B) | AlMg1 | 3.3315
Markings of aluminum and aluminum alloys according to various standards:
| Alu/Alloy | AW-5005 |
| AA | 5005 |
| PN | - |
| CSN | - |
| ASTM USA | 5005 |
| BS GB | 5005 |
| BS GP old | N41 |
| EN | AlMg1(B) |
| DIN GER | AlMg1 |
| EN | 5005 |
| ISO | AlMg1B |
| JIS JAPAN | A5005 |
| JIS JAPAN old | - |
| NF FRANCE | 5005 |
| NF FRANCE old | A-G0.6 |
| SFS FINLAND | 2586 |
| SN SWITZ | - |
| SS SWEDEN | 4106 |
| UNI ITALY | 9005/1 |
| UNI ITALY old | 5764 |
| UNS | A95005 |
| WNR GERMANY | 3.3315 |
| NS | - |
| UNE | - |
| ASV | - |
| ALUSUISSE | - |
| CSA old | - |
| GOST old | - |
Chemical composition of aluminum and aluminum alloys (according to EN 573-1):
| Alu/Alloy | AW-5005 |
| Mg | 0,50 - 1,10 [%] |
| Mn | ≤0,20 [%] |
| Fe | ≤0,70 [%] |
| Si | ≤0,30 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,20 [%] |
| Zn | ≤0,25 [%] |
| Cr | ≤0,10 [%] |
| Mn+Cr | - [%] |
| Ti | - [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Other | ≤0,05 [%] |
| different together | ≤0,15 [%] |
| Al | reszta |
Physical Properties of Aluminum:
| Alloy - Temper | AW-5005 |
| Density | 2.7 [g/cm3] |
| E modulus of elasticity | 69500 [MPa] |
| Shear modulus G | 26100 [MPa] |
| Poissons number | 0.33 |
| Solidification temperature | 630 [°C] |
| Pour point | 655 [°C] |
| The right warmth | 897 [J/kgK] |
| Coefficient of thermal expansion at 20°C | 23.5 [µm/mK] |
| Specific resistance | 33 [nWm] |
| Thermal conductivity | 201 [W/mK] |
| Conductivity | 52 [%IACS] |