ALUMINIUM AW-5083 | AlMg4,5Mn0,7 | AW-AlMg4,5Mn0,7 | AlMg4,5Mn | 3.3547
Markings of aluminum and aluminum alloys according to various standards:
| Alu/Alloy | AW-5083 |
| AA | 5083 |
| PN | PA13 |
| CSN | - |
| ASTM USA | 5083 |
| BS GB | 5083 |
| BS GP old | N8 |
| EN | AlMg4,5Mn0,7 |
| DIN GER | AlMg4,5Mn |
| EN | 5083 |
| ISO | AlMg4,5Mn0,7 |
| JIS JAPAN | A5083 |
| JIS JAPAN old | A2x7 |
| NF FRANCE | 5083 |
| NF FRANCE old | A-G4.5MC |
| SFS FINLAND | - |
| SN SWITZ | AlMg4,5Mn |
| SS SWEDEN | 4140 |
| UNI ITALY | 9005/5 |
| UNI ITALY old | 7790 |
| UNS | A95083 |
| WNR GERMANY | 3.3547 |
| NS | 17215 |
| UNE | L-3321 |
| ASV | 2021 |
| ALUSUISSE | 5460 |
| CSA old | GM41 |
| GOST old | - |
Chemical composition of aluminum and aluminum alloys (according to EN 573-1):
| Alu/Alloy | AW-5083 |
| Mg | 4,00 - 4,90 [%] |
| Mn | 0,40 - 1,00 [%] |
| Fe | ≤0,40 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,25 [%] |
| Cr | 0,05 - 0,25 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,15 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Other | ≤0,05 [%] |
| different together | ≤0,15 [%] |
| Al | reszta |
Physical Properties of Aluminum:
| Alloy - Temper | AW-5083 |
| Density | 2.7 [g/cm3] |
| E modulus of elasticity | 71000 [MPa] |
| Shear modulus G | 26800 [MPa] |
| Poissons number | 0.33 |
| Solidification temperature | 580 [°C] |
| Pour point | 640 [°C] |
| The right warmth | 899 [J/kgK] |
| Coefficient of thermal expansion at 20°C | 23.8 [µm/mK] |
| Specific resistance | 60 [nWm] |
| Thermal conductivity | 117 [W/mK] |
| Conductivity | 28.5 [%IACS] |