ALUMINIUM AW-5086 | AlMg4 | AW-AlMg4 | AlMg4Mn | 3.3545
Markings of aluminum and aluminum alloys according to various standards:
| Alu/Alloy | AW-5086 |
| AA | 5086 |
| PN | - |
| CSN | - |
| ASTM USA | 5086 |
| BS GB | - |
| BS GP old | - |
| EN | AlMg4 |
| DIN GER | AlMg4Mn |
| EN | 5086 |
| ISO | AlMg4 |
| JIS JAPAN | A5086 |
| JIS JAPAN old | - |
| NF FRANCE | 5086 |
| NF FRANCE old | A-G4MC |
| SFS FINLAND | - |
| SN SWITZ | AlMg4Mn |
| SS SWEDEN | - |
| UNI ITALY | 9005/4 |
| UNI ITALY old | 5452 |
| UNS | A95086 |
| WNR GERMANY | 3.3545 |
| NS | - |
| UNE | L-3322 |
| ASV | 2028 |
| ALUSUISSE | 5410 |
| CSA old | - |
| GOST old | AMg4 |
Chemical composition of aluminum and aluminum alloys (according to EN 573-1):
| Alu/Alloy | AW-5086 |
| Mg | 3,50 - 4,50 [%] |
| Mn | 0,20 - 0,70 [%] |
| Fe | ≤0,50 [%] |
| Si | ≤0,40 [%] |
| Si+Fe | - [%] |
| Cu | ≤0,10 [%] |
| Zn | ≤0,25 [%] |
| Cr | 0,05 - 0,25 [%] |
| Mn+Cr | - [%] |
| Ti | ≤0,15 [%] |
| Bi | - [%] |
| Ni | - [%] |
| Pb | - [%] |
| Sn | - [%] |
| Zr | - [%] |
| Zr+Ti | - [%] |
| Other | ≤0,05 [%] |
| different together | ≤0,15 [%] |
| Al | reszta |
Physical Properties of Aluminum:
| Alloy - Temper | AW-5086 |
| Density | 2.7 [g/cm3] |
| E modulus of elasticity | 71000 [MPa] |
| Shear modulus G | 26700 [MPa] |
| Poissons number | 0.33 |
| Solidification temperature | 585 [°C] |
| Pour point | 640 [°C] |
| The right warmth | 900 [J/kgK] |
| Coefficient of thermal expansion at 20°C | 23.8 [µm/mK] |
| Specific resistance | 56 [nWm] |
| Thermal conductivity | 126 [W/mK] |
| Conductivity | 31 [%IACS] |